Why Should You Converse with Your Stampings?
Friends bring an unconscious patient into the emergency room. The ER doctor examines the patient and finds no cuts, broken bones, bleeding or other visual external injuries. Does the doctor send the unconscious patient home because no treatment is obvious? No—instead, he conducts batteries of tests on the patient, in effect asking the body of the unconscious patient a series of questions, to which the body responds with data. This data provides exact information about the body’s condition. The success of this “conversation” depends on the doctor asking the right questions, and having the equipment to decipher the answers. Often the problem does not lie with one single body function; rather it results from the interaction of several functions.
Fig. 1—Stamping has two areas with identical final strain distributions.
What questions to ask? While no tears are observed, one might ask if the stamping deformed into the yellow (danger) zone of the forming-limit diagram, where sporadic breakage is expected. To collect the relevant data, we use circle-gridded blanks or other surface-strain measurement techniques.
We might also look for steep strain gradients with highly localized thinning, which can cause major changes in elastic stresses and result in springback and dimensional changes. An ultrasonic thickness gauge can extract the required data from the stamping.
|Fig. 2—Two locations on the same stamping with identical final strain distributions exhibit widely different strain histories.
Are temperatures increasing in areas of severe deformation and causing a change in the effectiveness of the lubricant? We can track these temperature changes easily, for the die and the stamping, with a laser thermometer gun.
Looking at the total forming system, more than 50 inputs can affect the final characteristics of a stamped part. Most of these inputs interact with each other. Attempting to measure every input and gauge all of their interactions proves nearly impossible. Hence, we focus our “conversation” on the output of the system—the stamping.
Conducting a continuous conversation with your stamping can form the foundation of virtual forming, where an operator enters into the computer the design for a stamping and its die. The conversation begins immediately, with questions such as:
• Where are your hot spots?
• Do you like the properties of the specified material?
• If I change this blank contour, are you more comfortable?
The dialog continues until the stamping and the designer reach an agreement. Then the hard die produces an actual stamping, restarting the conversation:
• Are you exactly like the virtual stamping?
• Where are you different?
• Why are you different?
Consider this case study illustrating how a conversation with the stamping can solve a random breakage problem. Under investigation: two locations on the punch, A and B, 3 ft. apart. The two strain distributions, measured at full depth or home stamping, are nearly identical (Fig. 1). Location A appears stable and never fails, while location B experiences frequent breakage. The available data proves insufficient for identifying the problem, or a solution.
|Fig. 3—Strain history for Location A was uniformly controlled by a draw bead. Location B started with the blank freely sliding into the die. It then formed a buckle at 6 in. of stamping depth that greatly changed the final strain history.|
Step one is to identify the strain history by asking the stamping for a series of incremental hits or breakdown stampings (Fig. 2). Location A appears to have a constant rate of straining until the very end of the stroke, where the rate of straining decreases. Location B exhibits the opposite behavior, as forming begins later in the stroke and then increases its rate of straining as the stroke approaches home depth.
Next we extend both strain histories back to their starting points (Fig. 3). Location A begins straining as soon as the punch contacts the blank, with a constant rate of deformation. Approaching home depth, the geometry almost is complete and strain rate tapers to zero. In the blankholder we find a draw bead exerting a restraining force and creating constant blank movement into the die opening.However, material at location B does not strain for the first 3.2 in. of punch travel. In the absence of a draw bead, the blank slides into the die opening without deformation. This free flow causes the material to gather and elastically buckle, causing the blank to lock up in the binder. As such, all length-of-line must come from elongation over the punch, at a catch-up pace. Approaching home depth, the material flow rate spirals out of control. As a result, small changes in the 50-plus input variables can easily drive the strain above the failure limit. Ask the stamping what it needs at location B, and the answer is: “A good draw bead.” MF